    Product Description

    High Gloss Metal Poly Urethane Coating is an anti-corrosive liquid chemical solvent which is used to provide a shield over different types of objects to protect them against environmental attacks. It consist of an isocyanate group which acts as a base material for the production of this chemical. The solvent has a good reactivity helps to provide a good bonding between the additives and other constituents present to provide a uniformity and high adhesion with the surface on which it is going to be applied. High Gloss Metal Poly Urethane Coating provides excellent finish and high gloss with a good resistance against abrasion. 

    Product Description:

    Two component, air drying, acrylic aliphatic polyurethane coating.

    Features :

    • Excellent finish with high gloss.
    • Excellent colour & gloss retension.
    • Excellent outdoor durability.
    • Tough, abrasion resistant coating with excellent flow and leveling charecterestics.
    • Good resistance to chemicals and polluted environments.

    Technical details

    Color

    : Wide Range

    Gloss

    : High Gloss/ Matte

    Volume solids

    : Approx 50%.

    Recommended DFT / coat

    : 35 - 50 m

    Theoretical covering capacity

    : 13 to 15 m2/l @ 35m

    Curing time at 30C

    : Surface dry : 30 Mins.

    : Hard dry : 16 hours

    : Full cure : 7 days

    Shelf life (cool & dry place)

    : 12 months(min)

    Flash point

    : Base : < 28C

    : Hardener : < 28C

    Surface Preparation & Substrate Condition

    • Can be applied on epoxy primer, epoxy /polyurethane undercoat; surface must be dry & free from all surface contamination. Surface of aged epoxy coating should be sufficiently roughened prior to painting.
    • Substrate temperature should be at least 3C above dew point but not above 50C.
    • Stir the base and hardener separately to get an uniform mix, then add hardener slowly to the base slowly with constant stirring for quick homogenous mixing.

    Mixing ratio

    Base : Hardener :: 4:1(v/v)

    Induction time

    25 minutes

    Pot life at 30

    3 hours


    Application:

    Brush

    • Recommended thinner : Tufthin 9
    • Volume of thinner : 0 - 10 %

    Air spray

    • Recommended thinner : Tufthin 9.
    • Volume of thinner : 5 - 20 %
    • Nozzle orifice : 1.5 - 3.0 mm
    • Nozzle pressure : 0.3 - 0.4 MPas

    Airless spray

    • Recommended thinner : Tufthin 9
    • Volume of thinner : 0 - 15 %
    • Nozzle orifice : 0.41 - 0.48 mm
    • Nozzle pressure : 20 - 24 MPas



    Trade Information
    • Kolkata
    • Telegraphic Transfer (T/T), Cheque, Cash in Advance (CID), Cash Advance (CA)
    • 10000 Per Month
    • 1 Week
    • Yes
    • Contact us for information regarding our sample policy
    • All India
    • ISO 9001:2008
      Related Products
      Heat Resistant Aluminum Paint




      Send Inquiry
      Therma King Heat Resistant Aluminum Paint




      Send Inquiry
      High Build Epoxy Anti-Skid Finish Paint




      Send Inquiry
      Single Pack Aluminium Paint


      Send Inquiry
      Fire Resistant Paint


      Send Inquiry
      PolyUrethane Matte Finish Paint


      Send Inquiry
      right arrow
      left arrow
      Contact Us

      66, Paik Para First Row  Kolkata  West Bengal  India  +918037400744
      Phone :+918037400744